Compare

Home
Compare

Materials

Foams

Elastomers

Elastomers

Elastomers

Elastomers

Elastomers

Elastomers

Elastomers, Sealants & Pastes

Elastomers, Sealants & Pastes

Elastomers, Sealants & Pastes

Elastomers, Sealants & Pastes

Elastomers, Sealants & Pastes

Composite Resins

Composite Resins

Composite Resins

Composite Resins

Chemistry

Polyurethane

Polyurethane

Silicone

Silicone

Silicone

Silicone

Silicone

Silicone

Silicone

Silicone

Silicone

Silicone

Epoxy

Epoxy

Epoxy

Epoxy

Processes

Casting, Foaming

Casting

Casting, Sealing

—

Casting

Casting

Casting

Calendering

Calendering

Calendering

Sealing

Sealing

Composite stratification

Composite stratification

Composite stratification

Glazing, Composite stratification

Conditionnements

2 kg plastic drum, 5 kg plastic drum

—

—

—

—

—

—

—

—

—

—

—

—

—

—

—

Densité (g/L)

—

—

—

—

—

—

—

—

—

—

—

—

—

—

—

—

Hardnesses (Sh A)

—

—

—

—

—

—

—

—

—

—

—

—

—

—

—

—

Demoulding time - 20°C

—

15min

5min

—

50min

3h/12h

20min

—

—

—

—

—

—

—

—

—

Application

—

—

Molding or impression

Custom liners

Custom liners

—

Socket duplication

—

—

—

Orthoplasties, refills, masking

Orthoplasties, refills, masking

—

—

—

—

Hardness

—

—

29 ShA

—

16 ShA

—

approx. 65 ShA

35 ShA

—

—

20 ShA

35 ShA

85 ShD

85 ShD

85 ShD

85 ShD

Mix viscosity at 20°C

—

—

Thixotrope

—

—

—

—

—

—

—

—

—

450 mPa.s

450 mPa.s

1100 mPa.s

1130 mPa.s

Ratio

—

—

100 / 100

100 / 100

100 / 100

100 / 100

100 / 100

—

—

—

100 / 100

100 / 100

100 / 40

100 / 40

100 / 40

100 / 40

Elongation at break

—

—

500%

—

500%

300%

80%

Mini. 650%

mini. 500%

mini. 500%

—

—

—

—

—

—

Working time at 20°C

—

—

3min

—

30min

9min/20min

3min

—

—

—

—

—

—

—

—

—

Silicone Type

—

—

RTV

RTV

RTV

RTV

RTV

HTV

HTV

HTV

RTV

RTV

—

—

—

—

Réactivité

—

—

—

—

—

—

—

—

—

—

—

—

—

—

—

—

Post curing

—

—

—

—

—

—

—

1h à 110°C

1h à 110°C

1h à 110°C

—

—

See technical data sheet

—

See technical data sheet

See technical data sheet

Résistance à la rupture

—

—

—

—

—

—

—

—

—

—

—

—

—

—

—

—

Résistance au déchirement

—

—

—

—

—

—

—

—

—

—

—

—

—

—

—

—

Working time at 20°C

—

—

—

—

—

—

—

—

—

—

4 min

4 min

—

—

—

—

Temps de mélange-20°C

—

—

—

—

—

—

—

—

—

—

—

—

—

—

—

—

Bio based

—

—

—

—

—

—

—

—

—

—

—

—

45 %

45 %

32 %

34%

Tg (°C)

—

—

—

—

—

—

—

—

—

—

—

—

—

—

—

—